Hadfield Managanese Plates
Hadfield manganese plates & Sheets Supplier in Mumbai-India
Hadfield Manganese Steel Plates Widely known for its work hardening properties, are amenable to high-impact wear applications or those in which scratch abrasion is encountered. These hardened steel plates enhance almost five times the hardness of mild steel and almost three times the hardness of annealed stainless steel. Due to this, one can enjoy a longer lifespan and extended protection of their equipment and facilities.
Technical Specifications
• Tensile - 132,000 PSI
• Hardness - 250BHN
• Yield - 90,000 PSI
• Will Work Hardened to 500BHN
• Elongation - 12%
• Hardness - 250BHN
• Yield - 90,000 PSI
• Will Work Hardened to 500BHN
• Elongation - 12%
Features
• High Abrasion Resistance
• Non-Magnetic Properties
• Deep Uniform Hardness
• Provide Maximum Wear Life
• Excellent Toughness
• Non-Magnetic Properties
• Deep Uniform Hardness
• Provide Maximum Wear Life
• Excellent Toughness
Application Used in
• Quarries and constructions
• Mines
• Iron industry and foundry
• Concrete and brick works
• Scraps
• Automotive industries
• Mines
• Iron industry and foundry
• Concrete and brick works
• Scraps
• Automotive industries
Standards
| EURONORM | 1.3401 � X120Mn13 | DIN | W1.3401 |
| AFNOR | X120Mn13 | ASTM | A128 Gr B2 |
Chemical Analysis Typical values (% weight)
| C | Si | Mn | Mn | P |
| 1.13 | 0.40 | 13 | 0.003 | ≤ 0.20 |
Mechanical Properties
| Hardness HB | Yield Strength MPa | UTS MPa | El% | KCV 20�C (68�F) - J | |
| Typical Values | 220 | 380(55 KSI) | 940(136 KSI) | 40 | ≥ 112 J(≥ 83 ft.lbs) |
| Guaranteed Values* | 180/245 | 350(51 KSI) | 800(116 KSI) | 30 | 64 J(47 ft.lbs) |
Physical Properties
| Density * | Expansion Coeff. 0-600�C | Specific Heat | Electrical * Resistivity | Thermal * Conductivity | Magnetic * Permeability | |
| Metric US | 7.88 | 10 -6�C1 21.5 10 -60�F-1 19.9 |
J/Metric Kg. �C 502 BTU/lb�F .12 |
�O.m 75 �O.m 75 |
W/m. �C 13 BTU/hr.ft�F 7.3 |
�1.002 |