ASME SA 387 GRADE 12 Class 1
Engineered for use in elevated temperature service, is a chrome molybdenum carbon alloy steel for use in weldable pressure vessels and industrial boilers.
The material benefits from added chromium which provides excellent corrosion and oxidation resistance making it ideal for sour service applications in the oil and gas industry.
Equivalents
| BS | EN | ASTM/ASME | DIN |
| 620 B | 13 CRMO 45 | SA387-12-1 | 13 CRMO 44 |
Specifications for ASME SA387 Grade 12 Alloy Steel Plates
Chromium & Molybdenum content (according to the ASME specification)
| Designation | Nominal Chromium Content (%) |
Nominal Molybdenum Content (%) |
| SA387 Grade 12 | 1.00% | 0.50% |
Tensile Requirements for ASME SA387 Grade 12 Alloy Steel Plates Class 1 Plates
| Designation: | Requirement: | Grade 12 |
| SA387 Grade 12 | Tensile strength, ksi [MPA] | 65 to 85 [450 to 585] |
| Yield strength, min, ksi [MPa]/(0.2% offset) | 40 [275] | |
| Elongation in 8 in. [200mm], min % | 19 | |
| Elongation in 2 in. [50mm], min, % | 22 | |
| Reduction of area, min % | ––– |
Chemical Requirements for ASME SA387 Grade 12 Alloy Steel Plates
| Element | Chemical Composition (%) | |
| ASME SA387 Grade 12 | ||
| Carbon: | Heat Analysis: | 0.05 - 0.17 |
| Product Analysis: | 0.04 - 0.17 | |
| Manganese: | Heat Analysis: | 0.40 - 0.65 |
| Product Analysis: | 0.35 - 0.73 | |
| Phosphorus: | Heat Analysis: | 0.035 |
| Product Analysis: | 0.035 | |
| Sulphur (max): | Heat Analysis: | 0.035 |
| Product Analysis: | 0.035 | |
| Silicon: | Heat Analysis: | 0.15 - 0.40 |
| Product Analysis: | 0.13 - 0.45 | |
| Chromium: | Heat Analysis: | 0.80 - 1.15 |
| Product Analysis: | 0.74 - 1.21 | |
| Molybdenum: | Heat Analysis: | 0.45 - 0.60 |
| Product Analysis: | 0.40 - 0.65 |